Synthesis and Characterization of Cr-Doped Pb2Fe2O5 Thin Films by Reactive Magnetron Sputtering

Multiferroic materials, which exhibit simultaneous ferroelectricity, ferromagnetism, and ferro-elasticity, have attracted significant attention due to their multifunctional properties. Coupling between ferroelectric and magnetic properties has led to the development of non-volatile memory devices, transducers, magnetic field sensors, and other applications. Pb2Fe2O5 (PFO) is a promising multiferroic material due to it simultaneously exhibiting ferroelectricity and ferromagnetism at room temperature. Doping with aliovalent ions, such as Cr3+, has been proposed as an effective method for enhancing the ferroelectric and magnetic properties, consequently leading to the enhancement of multiferroic properties. The investigation shows that the lead ferrite phase (220) was present in all samples, but its abundance reduced with increasing synthesis temperature due to lead desorption. Dielectric measurements revealed that PFO films with highest Cr concentration had the highest polarization (P-r) of 72.2 mu C cm(-2). The study also found that the magnetization of PFO films was up to 9.510(-7)mu Am-2 at an ambient temperature of 5 K, and the magnetic ordering temperature was 363 K, corresponding to the magnetic ordering temperature of chromium oxides. The morphology of Cr doped PFO films changed with increasing chromium content, resulting in a reduction in grain size and an increase in the film density.(c) 2023 The Author(s). Published on behalf of The Electrochemical Society by IOP Publishing Limited. This is an open accessarticle distributed under the terms of the Creative Commons Attribution 4.0 License (CC BY,http://creativecommons.org/licenses/by/4.0/), which permits unrestricted reuse of the work in any medium, provided the original work is properly cited.

Automated summary

Multiferroic materials, such as Pb2Fe2O5 (PFO), have attracted attention due to their multifunctional properties. Doping with aliovalent ions, like Cr3+, has been proposed as an effective method for enhancing the ferroelectric and magnetic properties of PFO. The study shows that Cr-doped PFO films exhibit improved polarization and magnetization, while their morphology changes with increasing chromium content.