nanoparticles; waterborne polyurethane; UV aging; mechanical resistance; polyester fabrics
The aim of this research was to study the impact of different types of nanoparticles on the UV weathering resistance of polyurethane treatment in polyester-based fabrics. The results showed that the addition of nanoparticles significantly improved the puncturing strength of the fabric and reduced its deformability. However, after UV aging, the mechanical performance of both the neat fabric and PU-impregnated specimens decreased.
The goal of this research was to investigate the effect of different types of nanoparticles on the UV weathering resistance of polyurethane (PU) treatment in polyester-based fabrics. In this regard, zinc oxide nanoparticles (ZnO), hydrophilic silica nanoparticles (SiO2 (200)), hydrophobic silica nanoparticles (SiO2 (R812)), and carbon nanotubes (CNT) were mixed into a waterborne polyurethane dispersion and impregnated into textile samples. The puncturing resistance of the developed specimens was examined before and after UV-accelerated aging. The changes in chemical structure and surface appearance in nanoparticle-containing systems and after UV treatments were documented using microscopic pictures and infrared spectroscopy (in attenuated total reflectance mode). Polyurethane impregnation significantly enhanced the puncturing strength of the neat fabric and reduced the textile's ability to be deformed. However, after UV aging, mechanical performance was reduced both in the neat and PU-impregnated specimens. After UV treatment, the average puncture strength of all nanoparticle-containing systems was always greater than that of aged fabrics impregnated with PU alone. In all cases, infrared spectroscopy revealed some slight differences in the absorbance intensity of characteristic peaks for polyurethane polymer in specimens before and after UV rays, which could be related to probable degradation effects.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据