This study investigates the microstructural properties and corrosion behavior of magnesium with added RE elements (Y, La) in varying minors after casting and heat treatment. The results show the presence of three-phase structures, such as α-Mg, lamellae-like phases, and network-shaped eutectic compounds. The corrosion behavior is affected by the content of lanthanum, with an increase in crater structures and a decrease in corrosion resistance observed. The corrosion products formed by Y2O3 and Y(OH)3 contribute to the thickness of the corrosion film and act as a protective barrier.
In this study, the microstructural properties and corrosion behavior of RE elements (Y, La) added to magnesium in varying minors after casting and homogenization heat treatment were investigated. Three-phase structures, such as & alpha;-Mg, lamellae-like phases, and network-shaped eutectic compounds, were seen in the microstructure results. The dendrite-like phases were evenly distributed from the eutectic compounds to the interior of the & alpha;-Mg grains, while the eutectic compounds (& alpha;-Mg + Mg) RE (La/Y)) were distributed at the grain boundaries. According to the corrosion results, the typical hydroxide formation for lanthanum content caused the formation of crater structures in the material, and with the increase in lanthanum content, these crater structures increased both in depth and in density. In addition, the corrosion products formed by Y2O3 and Y(OH)(3) in the Mg-3.21Y-3.15 La alloy increased the thickness of the corrosion film and formed a barrier that protects the material against corrosion. The thinness of the protective barrier against corrosion in the Mg-4.71 Y-3.98 La alloy is due to the increased lanthanum and yttrium ratios. In addition, the corrosion resistance of both Mg-3.21Y-3.15 La and Mg-4.71 Y-3.98 La alloys decreases after homogenization. This negative effect on corrosion is due to the coaxial distribution of oxide/hydroxide layers formed by yttrium and lanthanum after homogenization.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据