DOI: 10.1016/j.tsf.2023.139947
关键词
Zinc oxide; Thin film; Aluminum content; Magnetron sputtering; Optical and electrical characterizations
Al-doped ZnO thin films were deposited using radio frequency magnetron cosputtering. The effect of Al content variation on the properties of the films was studied. The films showed a wurtzite crystalline structure and improved optical and electrical properties after annealing at 300 degrees C. The optimized properties were obtained for an Al content ranging from 1.5 to 5.5 at.%.
Al-doped ZnO thin films with varying Aluminium (Al) content were deposited by radio frequency magnetron cosputtering of two ZnO and Al targets in confocal configuration. A comprehensive study of the effect of Al content variation on the structural, optical and electrical properties were studied for as-deposited films and after an annealing step under controlled argon atmosphere. Chemical composition analyses, performed by both X-ray photoelectron spectroscopy and energy dispersive X-ray spectrometry, show an Al content variation in the deposited films in the 0-14 at.% range by varying the Al target power from 0 to 30 W, while the Zn target power was kept constant at 200 W. All deposited films exhibit a wurtzite crystalline structure and a decreasing crystalline quality for Al content above 5 at.% as shown by grazing incidence X-ray diffraction patterns. Atomic Force Microscopy analysis revealed films with homogeneous and dense surface morphology with roughness in the one nm range. Carrier concentration, resistivity and photoluminescence vary significantly with Al content in the ZnO films and appear optimized for an Al content window ranging from 1.5 to 5.5 at. %. Both optical and electrical properties are improved by a post-annealing at 300 degrees C under argon. A high figure of merit of 43.6 x 10-4 sq.& omega;-1 was obtained for the ZnO film with Al content of 3.6 at.% after annealing at 300 degrees C. Optimized properties are obtained for a higher Al content than the standard value of 2 at. % widely used in published works.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据