Flaky FeSiAl; Ferrite nanosheet; Magnetism; Microwave absorption
Magnetite nanosheet coated flaky FeSiAl alloy composite powder was successfully synthesized and its morphology, composition, crystal structure, magnetism and electromagnetic performance were systematically studied. The saturation magnetization of the composite powder decreased, with the CoFe2O4 coated sample exhibiting the highest saturation magnetization. The complex permittivity and dielectric loss of the composite powder increased, while the magnetic loss decreased.
Magnetite (MFe2O4, M = Mn, Zn, Ni, Co) nanosheet coated flaky FeSiAl alloy composite powder have been successfully synthesized. The morphology, composition, crystal structures, magnetism and electromagnetic performance of composite powder were studied systematically. Spinel ferrite nanosheet were prepared on the surface of flaky FeSiAl by hydroxide deposition decomposition. This structure will benefit the microwave multiple reflection loss. The saturation magnetization of the composite powder decreased with ferrite coating. The ZnFe2O4 coated composite exhibited higher saturation magnetization while the CoFe2O4 coated composite had the highest coercivity. Owing to the oxide coating, the complex permittivity and dielectric loss of the composite powder were evidently increased while the magnetic loss significantly decreased. Magnetic loss was dominant under 13 GHz and dielectric loss contributed equally as magnetic loss at higher frequency. Therefore, the composite powder attenuate the electromagnetic waves much more efficiently at higher frequency. Our results provide a reference to understand the effect of ferrite nanosheet coating on the magnetism and design the microwave absorption of composite powder materials.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据