Fe-ZSM-5 zeolite membrane catalyst; Catalytic wet peroxide oxidation; Phenol; Membrane reactor
资金
- National Natural Science Foundation of China [21176086, 21376101]
Novel Fe-ZSM-5 zeolite membrane catalysts were prepared for catalytic wet peroxide oxidation (CWPO) of phenol in a membrane reactor. Firstly, the ZSM-5 zeolite membrane with a Si/Al ratio of 80 was fabricated by using secondary growth process on the surfaces of paper-like sintered stainless steel fibers (PSSFs) which was prepared by wet lay-up papermaking process and sintering process. Then, Fe-ZSM-5 zeolite membrane catalysts with Fe loading of 15%, 25% and 35% were prepared and systematically characterized by using X-ray diffraction (XRD), N-2 adsorption-desorption, field emission scanning electron microscopy (FE-SEM), energy-dispersive X-ray spectroscopy (EDS), H-2-temperature programmed reduction (H-2-TPR) and X-ray photoelectron spectra (XPS), respectively. Finally, catalytic activity of Fe-ZSM-5 zeolite membrane catalysts was evaluated by investigating the conversion of phenol, H2O2 and TOC as well as the Fe leaching concentration in the treated effluent based on the CWPO processes in a membrane reactor. The characterization results showed that ZSM-5 zeolite membrane with a thickness of 6 mu m was fabricated on the surface of PSSFs and Fe element with a form of Fe2O3 was uniformly dispersed on the surface of ZSM-5 zeolite membrane support. The results of CWPO of phenol showed that the catalyst with Fe loading around 25% achieved the highest activity (phenol conversion about 95% and TOC conversion about 45%, respectively) after continuously ran for 7 h. Meanwhile, low loss of Fe species was observed on all of the catalysts (Fe leaching concentration lower than 7 mg/L). (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据