4.7 Article

On the microstructure and high cycle fatigue of near-net shape PM-HIPed Inconel 625

出版社

ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2023.145671

关键词

Inconel 625; Microstructure; Fatigue properties; Mechanical properties; Surface roughness

向作者/读者索取更多资源

This paper investigates the microstructure and fatigue behavior of PM-HIPed Inconel 625. The samples show good tensile properties with high elongation despite the presence of carbonitrides. The fatigue strength of pickled samples is found to be 6% lower with higher standard deviation compared to machined samples, indicating different fatigue failure mechanisms.
This paper investigated the microstructure and fatigue behavior of PM-HIPed Inconel 625. The microstructure was composed of gamma phase and (Mo, Nb) carbonitrides located mostly on prior particle boundaries. Despite the presence of these carbonitrides, the samples showed good tensile properties with high elongation. Two different surface conditions, pickled and machined, were used for high cycle fatigue testing under a four-point bending test. The results indicated that pickled samples had 6% lower fatigue strength (at 106 cycles) with three times higher standard deviation compared to the machined ones. Fatigue failure mechanisms were found to be dependent on surface conditions and showed different failure modes due to non-metallic oxide inclusions and surface defects in samples with machined and pickled surfaces, respectively. The effect of type, size, and location of defects, multiplicity of crack initiations, as well as surface roughness were analyzed and discussed.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据