Friction stir processing; Laser directed energy deposition; AerMet100 steel; Strength; Ductility
The mechanical properties of AerMet100 steel fabricated by laser directed energy deposition (LDED) are adversely affected due to typical defects. Friction stir processing as a post treatment can effectively reduce porosity and enhance tensile properties, improving the overall performance of the steel.
Due to thick columnar crystals and obvious pores as typical defects, the mechanical properties of AerMet100 steel fabricated by laser directed energy deposition (LDED) are adversely affected, limiting its applicability in aerospace industry. Aiming at both defects, we developed friction stir processing as a post treatment to strengthen the LDEDed specimens, with two following advantages: (i) it significantly reduced the porosity and homogenized the microstructure, and the average grain size was decreased from 4.75 mu m to 1.24 mu m; and (ii) it significantly enhanced room temperature tensile properties by eliminating the pores, leading to the fact that the elongation increased from 3.51% to 7.38%, and the ultimate tensile strength increased from 1458 MPa to 1561 MPa. Therefore, FSP generated a simultaneous improvement in both the strength and elongation of the LDEDed AerMet100 steel.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据