Fabrication and application of network-liked carbon coated SiO as anode material for lithium ion batteries

期刊

MATERIALS LETTERS
卷 345, 期 -, 页码 -

出版社

ELSEVIER
DOI: 10.1016/j.matlet.2023.134446

关键词

Lithium-ion battery; SiO/C composite; Energy storage and conversion; Anode; Carbon coating

向作者/读者索取更多资源

SiO/carbon composite with network-liked carbon coating layer was prepared using a two-step spray-drying and subsequent pyrolysis method. This structure not only effectively prolongs the cycle performance but also greatly improves the rate capability. The obtained composite shows a reversible capacity of 1119.4mAh.g(-1) after 100 cycles at a current density of 200 mA.g(-1). Increasing the current densities to 500 mA.g(-1) and 1000 mA.g(-1), the capacity can still maintain at 887.2mAh.g(-1) and 577.7mAh.g(-1), respectively, indicating the network-liked carbon coated SiO reported in this paper is a promising anode material for lithium-ion batteries.
SiO/carbon composite with the network-liked carbon coating layer is prepared by a two-step spray-drying and subsequent pyrolysis method. Such a structure can not only effectively prolongs the cycle performance but also greatly improves the rate capability of the product. As a result, the obtained composite shows a reversible capacity of 1119.4mAh.g(-1) after 100 cycles at a current density of 200 mA.g(-1). Increasing the current densities to 500 mA.g(-1) and 1000 mA.g(-1), the capacity can still maintain 887.2mAh.g(-1) and 577.7mAh.g(-1), respectively, which indicate that the network-liked carbon coated SiO reported in this paper is a promising anode material for lithium-ion batteries.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据