JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 44, 期 3, 页码 1772-1782出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2023.10.038
关键词
Helical dislocation; Corundum precipitate; Dislocation in rutile; Alumina solid solution in rutile
Diffusion couples of rutile and corundum single crystals were prepared and examined to study the solid solution and precipitation of corundum in rutile during cooling. Different precipitation forms of corundum were observed under different cooling conditions.
Diffusion couples of rutile and corundum single crystals were prepared and examined for the solid solution and precipitation of corundum in rutile during cooling. Alumina dissolves in rutile according to the following equation, Al2O3 -> 2AlTi '+3OO+V-o(center dot center dot). In the sample air-quenched from 1200 degrees C, the supersaturated oxide ion vacancies, V-o(center dot center dot), reacted with the edge component of screw dislocation parallel to c axis to form helical dislocations, along which corundum was precipitated. When air-quenched from 1300 degrees C and 1400 degrees C, corundum was precipitated in the form of stacked rectangular loops. Corundum grains with eight lobes extending in the < 101 > directions were precipitated in the samples cooled at 10 degrees C/min from 1300 degrees C and 1400 degrees C. The solid solution reaction increased the volume of rutile single crystals and caused voids outside the reaction region at the interface. Both the corundum and rutile components of the voids also contributed to the solid solution reaction.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据