Formulating an altered dentin substrate to improve dentin bonding

期刊

JOURNAL OF PROSTHETIC DENTISTRY
卷 130, 期 5, 页码 -

出版社

MOSBY-ELSEVIER
DOI: 10.1016/j.prosdent.2023.07.024

关键词

-

向作者/读者索取更多资源

This study found that compared with NaF-containing etchant, SnF2-containing etchant could improve the dentin substrate, increase remineralization, improve bonding strength, and enhance antibacterial ability, especially by increasing resistance to acid erosion.
Statement of problem. Secondary caries is a major factor in the failure of dental restorations. However, studies on the fabrication of acid-resistant and antibacterial dentin to improve dentin bonding are sparse.Purpose. The purpose of this in vitro study was to compare the effects of 2 types of fluoride-containing etchants on dentin bonding and explore the feasibility of formulating an altered dentin substrate to improve dentin bonding.Material and methods. NaF-containing and SnF2-containing etchants were developed by adding sodium fluoride and stannous fluoride to a 35% phosphoric acid aqueous solution. Two groups (N1 and N2) containing NaF, 10 and 30 mg/mL respectively, and 2 groups (S1 and S2) containing SnF2, 18.6 and 55.8 mg/mL respectively, were formulated. The etchant of the control group (C) was 35% phosphoric acid gel. Scanning electron microscopy (SEM), energy dispersive spectrometry (EDS), Fourier transform infrared spectroscopy (FTIR), microhardness, antierosion, and antibacterial tests were performed on the treated dentin. Moreover, the microtensile bond strength (mu TBS) of each group was tested, and the fracture mode was determined after testing. Statistical analysis was performed with the 2-way ANOVA test (alpha=.05).Results. The exposed collagen fiber was observed in group C, and minerals were formed on the dentin in the experimental groups. SEM, FTIR, and the microhardness test indicated more remineralization in the SnF2-containing etchant groups. The mu TBS of S1 (77.5 +/- 10.36 MPa) was the highest in all groups, and group C (38.5 +/- 9.01 MPa) was the lowest. Moreover, the antierosion and antibacterial properties of the S2 group were the best among all groups (P<.05).Conclusions. Compared with NaF-containing etchant, SnF2-containing etchant could improve the dentin substrate, increase remineralization, improve bonding strength, and enhance antibacterial ability, especially by increasing resistance to acid erosion.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.5
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据