关键词
Additive manufacturing; Magnetron sputtering; Laser powder bed fusion; Physical vapour deposition
Coating powders with an optically absorptive layer improves the melting performance and uniform densification of highly reflective and high thermally conductive materials during laser powder bed fusion (LPBF). In-situ alloying of coated Ag powder with Ti also showed improved absorptivity and uniform densification, offering a promising route for improved alloy development via LPBF.
Processing of highly reflective and high thermally conductive materials (Cu, Ag, etc.) by laser powder bed fusion (LPBF) is of increasing interest to broaden the range of materials that can be additively manufactured. However, these alloys are challenged by high reflectivity resulting in unmelted particles and porosity. This is exacerbated for in-situ alloying techniques, where divergent optical properties of blended powders further narrow the stable processing window. One possible route to improved uniformity of initial melting is through coating powders with an optically absorptive layer. In-situ alloying of Ti-Ag was chosen as a model to assess this, given the potential of Ti-Ag as a novel antimicrobial biomedical alloy, facilitating an ideal model to assess this approach. High purity Ag powder was coated with Ti via physical vapour deposition. Barriers to reliable coating were investigated, with agglomeration of particles observed at a sputtering power of 100 W. In-situ laser micro calorimetry demonstrated a significant improvement in melting performance for coated Ag powder, with continuous tracks attained at 280 W vs. 320 W for uncoated powder, and absorptivity increasing from 27 % to 45 % at 320 W incident laser power. Subsequent in-situ alloying of the Ag powder when blended with commercially pure Ti powder demonstrated that improved absorptivity allowed for more uniform densification of the blended powder bed at lower energy density (0.7 & PLUSMN; 1.0 vs 7.1 & PLUSMN; 2.0 % porosity at 133 J.m-1). Ultimately, this offers a promising route to improved alloy development via LPBF, through application of a homogeneous, relevant coating.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据