A novel blended polymer membrane is prepared for vanadium redox flow batteries (VRFBs) as the diaphragm, which possesses superior affinity to sulfuric acid due to acid-base interactions. The membrane exhibits high oxidation stability and low vanadium permeability. The VRFB assembled with this membrane shows energy efficiency above 82% at a current density range of 20 to 120 mA cm-2 and stable performance after 50 charge-discharge cycles.
A novel blended polymer membrane is prepared by a facile route for using as the diaphragm in vanadium redox flow batteries (VRFBs). The polymers polyvinylchloride (PVC) and polyvinylpyrrolidone (PVP) are first blended in a 1.2:1 mol ratio to give a PVP-PVC mixture, and the PVC in the mixture is then functionalized with 1-(3-aminopropyl)-imidazole (APIm). The functionalized polymers are impregnated into the porous polytetrafluoroethylene (PTFE) to fabricate membranes. The obtained membranes possess superior affinity to sulfuric acid mainly due to acid-base interactions between APIm groups and sulfuric acid molecules. The presence of hydrophobic PTFE restricts the deterioration of mechanical strength of membranes by doped acids. Moreover, the prepared membranes exhibit high oxidation stability and low vanadium permeability. The VRFB assembled with the proposed diaphragm displays energy efficiency above 82 % at a current density range of 20 to 120 mA cm-2. The membrane-based VRFB demonstrates stable performance after over 50 charge-discharge cycles.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据