4.7 Article

Study on glass-ceramic prepared by zinc leaching residue and solidification mechanism of heavy metals

期刊

JOURNAL OF CLEANER PRODUCTION
卷 426, 期 -, 页码 -

出版社

ELSEVIER SCI LTD
DOI: 10.1016/j.jclepro.2023.139021

关键词

Zinc leaching residue; Glass-ceramic; Heavy metals; Solidification

向作者/读者索取更多资源

This paper introduces a micro-crystallization method to process zinc leaching residue into glass-ceramics with excellent performance and high value. The glass-ceramics effectively solidify heavy metals, eliminating their high hazard, and exhibit excellent mechanical and corrosion resistance properties.
Zinc leaching residue is a hazardous solid waste with difficult treatment, high hazard and high yield, and it is a great challenge to treat it efficiently, harmlessly and economically among the various methods available. This paper introduced a micro-crystallization method to process zinc leaching residue into glass-ceramics with excellent performance and high value. The heavy metals in the raw material were well solidified in the glass -ceramics, eliminating the high hazard of heavy metals and other components. The bending strength, compres-sive strength, and Vickers hardness of the glass-ceramics prepared at the sintering temperature of 950 degrees C were 69.2 MPa, 434.3 MPa, and 6.66 GPa, respectively, while the water absorption, density, and acid and alkali corrosion resistance were excellent. The relationship between the microstructure and properties of glass-ceramics was investigated using traditional analytical techniques such as XRD, Raman, and SEM, and the mechanism of solidification of heavy metals Pb, Zn and Mn in glass ceramics were innovatively researched by the modified BCR sequential leaching test and XPS analysis. Anorthite and diopside ferrian were the two main crystalline phases in glass-ceramics. The sintering temperature affected the formation and growth of crystals, and determined the crystal size and crystallization rate, thus affecting the properties of glass-ceramics. Part of the heavy metal was solidified in the amorphous phase in the glass-ceramic, and the other major part entered the crystal as an im-purity substitution to form a solid solution at a specific location. The zinc leaching residue based glass-ceramic had been studied, which was pioneering and with excellent performance and environmental safety. Thus, the safe and economical treatment of these hazardous wastes promotes the clean, green and efficient development of related industries.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据