Preparation and performance investigation of high solid content flame retardant waterborne polyurethane

期刊

出版社

WILEY
DOI: 10.1002/app.54674

关键词

flame resistance; high solid content; waterborne polyurethane

向作者/读者索取更多资源

In order to enhance the flame retardancy and solid content of waterborne polyurethane (WPU), AOT and AOD series of WPU were synthesized and characterized. Carboxylic acid/nonionic composite units were used as hydrophilic groups, and OP550/THPO and OP550/DOPO-HQ combinations were used as flame retardant modifiers, respectively. The modified WPU emulsions displayed excellent dispersion, stability, and fluidity, with a UL-94 rating of V-0. The AOD series samples showed better flame retardancy than the AOT series, particularly AO(10)D(3)-WPU containing 3% DOPO-HQ, which achieved a limiting oxygen index value of 30.5%. Additionally, the flame retardants promoted carbon formation in the condensed phase.
To improve the flame retardancy and solid content of waterborne polyurethane (WPU), AOT, and AOD series of WPU were synthesized and characterized. Carboxylic acid/nonionic composite units were used as hydrophilic groups, and OP550/THPO and OP550/DOPO-HQ combinations were used as flame retardant modifiers, respectively. The results revealed that the flame retardant-modified WPU emulsions still had excellent dispersion, stability, and fluidity. The UL-94 rating of modified WPU could reach V-0, and the AOD series samples had better flame retardancy than the AOT series, where AO(10)D(3)-WPU containing 3% DOPO-HQ had an limiting oxygen index value up to 30.5%. Besides, the peak heat release rate and total heat release of AO(10)D(3)-WPU were respectively decreased by 32% and 34%, compared with the control sample in the conical calorimetric test. The TGA, TG-IR, and SEM-EDS exhibited that the flame retardants functioned in the condensed phase by promoting carbon formation. The tensile strength of AOT series samples was excellent with a range of 15.84-27.47 MPa, while the elongation at break of AOD series samples was relatively high with a distribution of 850.8%-913.11%, which could be selected to suit the needs of different application scenarios.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据