Inception of macroscopic shear bands during hot working of aluminum alloys

期刊

INTERNATIONAL JOURNAL OF PLASTICITY
卷 166, 期 -, 页码 -

出版社

PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.ijplas.2023.103632

关键词

Aluminum; Deformation; Microstructure; Macroscopic shear band; Modelling

向作者/读者索取更多资源

Macroscopic shear bands (MSB) may form during hot working of metallic materials. The microstructural transitions between the onset of flow instability and MSB inception are not fully understood. In this study, aluminum alloy specimens were tested at different temperatures and it was found that MSB only appeared at a certain level of deformation. The formation of MSB was explained by the development of clusters of severely deforming grains and the differential dynamic recovery between hard- and soft-oriented grains.
Macroscopic shear bands (MSB) may develop during hot working of metallic materials. They are well-understood as a physical manifestation of flow instability, and the processing regimes wherein they form are well-charted. However, the microstructural transitions that occur between the onset of flow instability and MSB inception are not fully understood. In order to elucidate them, several aluminum alloy specimens were subjected to strip testing in a thermomechanical simulator (GleebleTM) at 298 K and 573 K. Prominent MSB were observed along the diagonals of the strip volume of only Aluminum-6 wt% Magnesium alloy specimen deformed at 573 K. Comparing the experimental grain morphology and crystallographic textures with those from plastic flow models revealed that MSB inception occurred only after similar to 0.20 homogeneous plane strain deformation. However, classical flow instability was predicted at much smaller strain. This 'delay' was explained experimentally by showing that clusters of neighbouring severely deforming, fragmenting, mostly soft-oriented grains gradually developed due to lattice rotations along the specimen diagonals, and that MSB inception corresponded to the formation of a percolating network of such grains spanning the specimen. Further, clear experimental evidence revealed that differential dynamic recovery between hard- and soft-oriented grains was essential for MSB formation.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据