期刊
INORGANIC CHEMISTRY
卷 62, 期 40, 页码 16323-16328出版社
AMER CHEMICAL SOC
DOI: 10.1021/acs.inorgchem.3c01311
关键词
-
This study reports the easy and low-cost synthesis of calcium niobate (CaNb2O6) with the isomorphic structure of the Rynersonite mineral. The samples were prepared by the ball milling method at room temperature in a short synthesis time, and showed strong photon absorption in the UVA region of the spectrum.
In this study, we report the easy and low-cost synthesis of calcium niobate (CaNb2O6) with the isomorphic structure of the Rynersonite mineral for CaTa2O6. The samples were prepared by the ball milling method at room temperature at a synthesis time of 0.5, 1, 2, 3, and 4 h. The structural analysis by XRD, Rietveld refinement, and vibrational Raman spectroscopy confirms all diffraction peaks and active mode characteristics of the pure phase of CaNb2O6 for the 3-h and 4-h samples, with a crystallite size of 22.5 and 23.2 nm, respectively. The optical band gap obtained was 3.18(2) eV (3-h sample), lower than the optical band gap for niobium oxide, characteristic of materials with strong photon absorption in the UVA region of the spectrum. The surface analysis by scanning electron microscopy reveals the obtention of several agglomerates of irregular particles ranging in the submicro and micro scales. Therefore, the present approach successfully obtained calcium niobate with the formula CaNb2O6 at a short synthesis time and room temperature.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据