Redox on Mn-Ce interface and its effects on low temperature selective catalytic reduction for NOx removal

The objective of this work was to clearly elucidate the interactions on Mn-Ce interface and understand how they affect low temperature selective catalytic reduction (SCR) for NOx removal. In this work, three Mn-Ce catalysts in similar particle size and morphology with different Mn-Ce interface areas were prepared. MnO2@CeO2-F had the tightest and largest amount of Mn-Ce interfaces compared with MnO2@CeO2-P and MnO2-CeO2-M, and also exhibited the highest NO conversion degree at 100-150 degrees C as well as the strongest activity of Mn species and lowest generation of N2O. The TG-DTG, XPS and electrochemical impedance spectroscopy results proved the redox of Ce4+ + Mn3+ & LRARR; Ce3+ + Mn4+ on the Mn-Ce interface, and MnO2@CeO2-F had the highest Mn4+, Ce3+, O & alpha; concentrations. The results of the study on the redox reactions during the NH3-SCR process provided powerful evidence of the Mn4+/Mn3+ and Ce3+/Ce4+ recycles that are important for low temperature NH3-SCR process. Moreover, the Mn-Ce interface was directly proved to benefit the surface acid sites, redox ability, and activity of the adsorbed intermediates. Both the Eley-Rideal (E-R) and Langmuir-Hinshelwood (L-H) reaction mechanisms were observed in the SCR reaction with prepared Mn-Ce materials, where fast SCR can be observed with MnO2@CeO2-F. Moreover, the Mn-Ce interface also lowers the activation energy of the low-temperature SCR process, with MnO2@CeO2-F having the lowest activation energy. The results from this work offered powerful evidences for the interactions of Mn/Ce redox at the Mn-Ce interface and elucidated clear understanding of the effects of Mn-Ce redox on low-temperature SCR process, which is expected to promote the NOx removal process.

Automated summary

The aim of this study was to investigate the interactions on Mn-Ce interface and their influence on low temperature selective catalytic reduction (SCR) for NOx removal. Three Mn-Ce catalysts with similar particle size and morphology but different Mn-Ce interface areas were prepared. MnO2@CeO2-F showed the tightest and largest amount of Mn-Ce interfaces, exhibiting the highest NO conversion degree, strongest activity of Mn species, and lowest generation of N2O. The results provided strong evidence for the importance of Mn/Ce redox and clarified the effects of Mn-Ce redox on low-temperature SCR process.