CORROSION SCIENCE
卷 226, 期 -, 页码 -出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.corsci.2023.111648
关键词
C/C-ZrC-SiC composites; SiC-C interphase; Mechanical property; Ablation performance
By introducing a tailored SiC-C interphase, the carbon fiber can be effectively protected, improving the mechanical and ablation properties of leading edge shaped C/C-ZrC-SiC composites.
To mitigate interphase degradation and improve the mechanical and ablation properties of leading edge shaped C/C-ZrC-SiC composites fabricated by reactive melt infiltration, a tailored SiC-C interphase composed of SiC, gas pyrolysis carbon and phenolic resin pyrolysis char was introduced. The SiC-C interphase can effectively protect the carbon fiber from high-temperature melt erosion, improving the flexural strength of the composites by 98%. The mass and thickness change rates of the leading edge composites were 2.96 +/- 0.04 mu m/s and - 0.42 +/- 0.04 mg/s, respectively. The better ablation performance was attributed to the synergistic effect of dense and stabilized Zr-Si-O oxide layer formation and heat transfer.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据