A green and environmentally friendly biomass intumescent flame retardant and smoke suppressed PAN fibers were developed by blending with PA@SE and VB2. The tensile strength and elongation at break of PAN-10%PA@SE/5%VB2 increased significantly, while the peak heat release rate (PHRR) and total smoke production (TSP) were significantly reduced. Additionally, a flame retardant PAN (PANC) was prepared and showed excellent compatibility with cellulose and PVA, greatly improving fire safety for these polymers.
A green, environmental-friendly biomass intumescent flame retardant and smoke suppressed polyacrylonitrile (PAN) fibers was developed by blending with PA@SE reacted by phytic acid (PA) and serine (SE) and vitamin b2 (VB2). Compared with the original sample, the tensile strength and elongation at break for PAN-10%PA@SE/5% VB2 increased by 22.3% and 68.2% respectively; The peak heat release rate (PHRR) and total smoke production (TSP) had 57.4% and 65.4% reduction. Furthermore, to make full use of potential waste flame retardant PAN, the char of flame retardant PAN (PANC) was prepared, which showed excellent compatibility with cellulose and polyvinyl alcohol (PVA). Compared to blank samples, the maximum thermal decomposition rate and heat release capacity for PANC@Cellulose and PANC@PVA decreased significantly, and the fire safety for these polymers was significantly increased. This work not only prepared flame retardant PAN materials, but also provided a feasible way for the recycling of waste flame retardant PAN materials.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据