Mechanisms for high creep resistance in alumina forming austenitic (AFA) alloys

Castable alumina forming austenitic (AFA) alloys have demonstrated superior creep life and oxidation resistance at temperatures exceeding 800 degrees C. Despite the success in the applicability of these alloys in extreme environments, there is a limited understanding of the deformation modes and the influence of each alloying element guiding the alloy design strategies that could further enhance the creep strength of these AFA alloys, particularly at temperatures at and above 900 degrees C. In this study, we reveal the mechanism underpinning the superior creep performance of castable AFA alloys that involves suppressing primary carbide formation through minor compositional modification. This approach results in a three-fold increase in creep strength at 900 degrees C and 50 MPa. By employing integrated characterization techniques, we analyzed the microstructures of two AFA alloys, both before and after the creep process. We discovered that the suppression of primary carbides permits the in-situ clustering of now-available interstitial elements such as C, Si, and O during high-temperature creep. This improved solid solution strengthening and reduced stacking fault energy of the alloy. Moreover, it also enabled controlled secondary carbide formation during testing, further improving the creep resistance. These findings underline the important interplay between alloy composition, microstructure, and creep properties, and offer a promising design strategy for developing economical high-temperature Fe-based alloys suitable for advanced applications.

Automated summary

Castable alumina forming austenitic alloys exhibit superior creep life and oxidation resistance at high temperatures. This study reveals the mechanism behind the enhanced creep performance of these alloys by suppressing primary carbide formation and offers a promising alloy design strategy for high-temperature applications.