DOI: 10.1016/j.msea.2016.05.112
关键词
Magnesium; Instrumented indentation test; {10(1)over-bar2} extension twins; 3D-EBSD; Crystal plasticity finite element analysis
类别
资金
- NSERC Magnesium Strategic Research Network
Instrumented spherical indentation has been used to extract information on the deformation behaviour of (0001) oriented grains in commercial purity magnesium. Reproducible discontinuities were found in the loading and the unloading curves and these have been interpreted as the nucleation and growth of {10 (1) over bar2) extension twins during loading and their subsequent retreat during unloading. Detailed three-dimensional electron backscatter diffraction-based orientation microscopy (3D-EBSD) revealed that the presence of residual deformation twins depended on the depth of the indent. Analysis of residual geometrically necessary dislocation density using the EBSD data showed that residual basal < a > dislocations were dominant in the deformation zone. The crystallographic misorientation observed below the indent can be rationalized by the presence of these basal < a > dislocations and this is shown to be consistent with crystal plasticity finite element method calculations. Finally, a schematic view of the different stages of deformation during loading and unloading is proposed to rationalize the experimental observations. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据