Ultra-rapid annealing; Grain refinement; Severe plastic deformation
类别
资金
- research board of Sharif University of Technology
Ultra-rapid annealing (URA) of deformed low-carbon steel can provide refined microstructure. In this research, severely deformed low-carbon steel is ultra-rapidly annealed to subcritical and intercritical temperature ranges at the heating rates of 75-1800 degrees C/s and then rapidly cooled. Also, conventional annealing by the heating rate of 0.3 degrees C/s is performed at the same temperature ranges. The results show that conventional and subcritical ultra-rapid annealing cannot lead to a fully refined microstructure. High heating rate causes the interaction between recrystallization and transformation as the temperature exceed Act (intercritical temperature range). High kinetics of transformation during intercritical ultra rapid annealing and interaction lead to the fully refined recrystallized microstructure. During subcritical conventional annealing of severely deformed sample, hardness is reduced gradually to the hardness of as-received sample. In contrast, URA increases the hardness in subcritical range due to solid solute carbon. Around Ac-1, hardness is dropped down because of accelerated recrystallization, and it is increased again in higher intercritical temperature due to increase of harder phases formed from austenite during cooling. Samples ultra-rapidly annealed in intercritical temperature range have higher hardness, strength and ductility than those of the samples annealed in subcritical range due to the presence of both types of ferrites; refined recrystallized primary ferrite and secondary ferrites formed from austenite during cooling after URA. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据