DOI: 10.1016/j.msea.2015.12.017
关键词
High entropy alloy; Brillouin light scattering; Sound velocity; Tensile test; Electron backscatter diffraction; Nanoindentation
Elastic properties of as-cast TiHfZrTaNb high entropy alloy were investigated by ultrasound measurements, yielding G=C-44=28 GPa and C-11=172 GPa effective isotropic elastic constants, allowing computation of the Young's modulus E, the bulk modulus B and Poisson ratio nu of about 78.5 GPa, 134.6 GPa and 0.402, respectively. A Pugh ratio G/B as lower as 0.208 and high positive Cauchy pressure (C-12-C-44)=80 GPa were calculated, suggesting a ductile behavior. Tensile tests were carried out on specimens taken along the ingot diameter to address micro-segregations effect on the macroscopic behavior. More specifically, micro-segregations were addressed at a smaller scale via nanohardness measurements. Given the observed low deviations from both tensile and nanoindentation experiments, micro-segregations influence was concluded to be negligible. The necking and fracture surface investigations revealed multiples slip bands, grains boundary distortions, mixture of shallow and profound dimples of varying sizes, all of which characterize a high tensile ductility behavior, in line with elasticity measurements prediction. Post-mortem EBSD investigations revealed lattice distortions mainly at grain boundaries vicinity as a consequence of dislocations accumulation. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据