Mg-4Zn-2Al-2Sn alloy; Hot deformation; Microstructural evolution; Dynamic recrystallization
类别
资金
- National Basic Research Program of China [2013CB632205]
- Shandong Provincial Natural Science Foundation, China [ZR2015YL007]
The dynamic microstructural evolution of the Mg-4Zn-2Al-2Sn (ZAT422) alloy during hot deformation was studied. The compression tests were carried out under the strain rate of 0.01 s(-1) and 5 s(-1) at 548 K and the strain rate of 5 s(-1) at 648 K. It was shown that the operating mechanisms of dynamic re crystallization (DRX) of ZAT422 alloy during hot deformation were affected by both strain rate and temperature. Parallel or crossed (1012) tension twins appeared in the sample deformed to the strain of 0.04 under the strain rate of 0.01 s(-1) at 548 K, while new grains with characteristics of discontinuous dynamic recrystallization (DDRX) occurred at corrugated grain boundaries. With the strain rate increasing from 0.01 s(-1) to 5 s(-1), the effect of twin dynamic recrystallization (TDRX) increased, and necklace structure of DRXed grains formed along the original grain boundaries and the deformation twin boundaries. When the temperature increased to 648 K, continuous dynamic recrystallization (CDRX) occurred within the recrystallized grains, resulting in the further refinement of the microstructure. And it should be noted that TDRX still occurred at this temperature. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据