MATERIALS SCIENCE & ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS
卷 58, 期 -, 页码 971-976出版社
ELSEVIER
DOI: 10.1016/j.msec.2015.09.047
关键词
Nano-sized beta-TCP granules; Wet chemical precipitation; Microstructure; Physical characterizations; Bone regeneration effect
The nano-sized p-tricalcium phosphate granules for the practical application of bone graft substitutes could be prepared from the wet chemically precipitated beta-TCP powders by the liquid-solid mixture route and by controlling the pH of mixture solution to 7.5 within a shorter processing time. The phase purity of prepared beta-TCP granules was higher above 99% and their particle sizes ranged from 200 to 650 nm. Also, their average compressive strength was higher at 222 MPa. It is considered that the phase purity, particle refinement, and mechanical compressive strength of beta-TCP granules could be significantly improved through the beta-TCP powders synthesized through the liquid-solid mixture precipitation at pH of 7.5. Meanwhile both the porosity and the specific surface area positively associated with the osteoconductivity for bone regeneration were higher at 75% and 2.50 m(2)/g respectively due to the nano-sized particles of porous beta-TCP granules. Furthermore, the histological analysis in beagle mandibular defect showed that beta-TCP granules demonstrated remarkable bone regeneration effectcompared with that of the non-treatment group, indicating the increased new formation of bone (except for callus) (48.42 +/- 6.57%) and rapid resorption (69.49 +/- 2.40%) without toxicologically significant changes at 12 weeks after implantation. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据