maraging 300; heat treatment; microstructure; toughness
Maraging 300 belongs to a family of metallic materials with extremely high mechanical strength and good toughness. Some works have been published about aging temperatures that improve ultimate strength resistance with acceptable toughness levels in this steel family, where the prior austenite grain size obtained by different solution annealing temperature influence in the final mechanical properties. Solution annealing temperatures ranging from 860 degrees C to 1150 degrees C and were kept constant until the aging temperature. These treatments were used in order to investigate their influence on the microstructure and mechanical properties of maraging steel 300, especially with regard to toughness. The characterization of the microstructure was performed by optical microscopy, scanning electron microscope (SEM) and X-ray diffraction (XRD). Mechanical properties were evaluated by Rockwell C hardness and Charpy impact tests. The results showed that there is a temperature range where one can get some improvement in toughness without a large loss of mechanical strength.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据