期刊
MATERIALS RESEARCH BULLETIN
卷 83, 期 -, 页码 400-407出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.materresbull.2016.06.032
关键词
Glasses; Inorganic compounds; Luminescence; Optical properties; XAFS; Electronic structure
资金
- Guangdong Natural Science Foundation [2014A030310132]
- Guangdong University Students Science and Technology Innovation Cultivation Special Fund [400160013]
- Guangdong University of Technology through the One-Hundred Young Talents Program start-up grant [220413505]
- University Students' Innovation and Entrepreneurship Training Program [yj201611845021]
Glasses from the lead borate system of the composition 50%PbO-50%B2O3 together with samples containing different concentrations of 3d-transition metal (TM) species from V to Zn were prepared by the melting-quenching technique and their optical properties were investigated. The X-ray absorption near edge spectra of V, Cr, and Mn-doped glasses indicates that the oxidation states of V(IV/V), Cr(III, VI) and Mn(II, III/IV) exist in the studied glasses. The oxidation states revealed from the diffuse reflectance spectra, absorption spectra, excitation and emission spectra of the glasses are V(IV), Cr(III, VI), Mn(II, III), Fe(II), Co(II), Ni(II), and Cu(lI). The undoped lead borate glass exhibits strong UV absorption which corresponds to interconfigurational transitions of Pb2+ and the host absorption, and intrinsic broad host emission at 470 nm using excitation at 350 nm. The 3d TM ions from V to Cu doped at high concentration (0.5 or 2 mol%) show additional distinctive strong absorption bands and a red-shifted absorption edge. The Mn2+ emission at 625 nm due to the T-4(1g)((4)G)->(6)A(1g)(S-6) spin-forbidden transition of octahedrally-coordinated Mn2+ was observed under excitation at 412 nm or 369 nm. (C) 2016 Elsevier Ltd. All rights reserved.