Magnetic properties; Mossbauer spectroscopy; X-ray diffraction; Transmission electron microscopy; Crystal structure
资金
- UGC-DAE CSR KC [UGC-DAE-CSR-KC/CRS/13/MS04/0814/0837]
- FIST programme [SR/FST/PSI-170/2011(C)]
- UGC, Govt. of India [F.530/5/CAS/2011]
Nanoparticles of Ni0.4Zn0.4Co0.2Fe2O4 are prepared by a simple co-precipitation method. The as dried sample is heat treated at 400, 500, 600, 700 and 800 degrees C to obtain different sizes of nanoparticles. The crystallographic phase of the samples is confirmed analyzing observed X-ray diffraction (XRD) by Rietveld method. Hyperfine parameters of the samples are derived from room temperature (RT) Mossbauer spectra of the samples. Magnetic properties of the samples are investigated by static and dynamic hysteresis loops. Different magneto-crystalline parameters are calculated from the variation of magnetization with temperature (M-T curve) under zero field cooled (ZFC) and field cooled (FC) conditions of the as dried sample. The cation distribution estimated from Rietveld analysis are correlated with the results of magnetic and Mossbauer effect measurements. The observed high value of saturation magnetization (72.7 emu/g at RT) of the sample annealed at 800 degrees C would be interesting for applications in different electromagnetic devices. (C) 2015 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据