卷 24, 期 1, 页码 106-113出版社
VASYL STEFANYK PRECARPATHIAN NATL UNIV
DOI: 10.15330/pcss.24.1.106-113
关键词
Co-based amorphous alloy; DTA; thermo-magnetic curves; hysteresis; magnetic properties; X-ray diffraction; nanocrystallization
The magnetic properties of the amorphous Co57Fe5Ni10Si11B17 alloy were investigated using a vibrating sample magnetometer. The temperature dependence of saturation magnetization was measured, and the Curie point and crystallization onset temperature were determined as 560 K and 760 K, respectively. The alloy was produced as a 30 μm thick ribbon using the melt spinning method, and its amorphous structure was examined using X-ray diffraction. The crystallization behavior of the alloy was studied by annealing the samples at temperatures ranging from 723 K to 1023 K.
The magnetic properties of the amorphous Co57Fe5Ni10Si11B17 alloy have been studied by a vibrating sample magnetometer. The temperature dependence of saturation magnetization was measured and the Curie point and crystallization onset temperature were determined as 560 K and 760 K respectively. The coercive force was obtained as 200 A/m and saturation magnetization - 65 Am-2/kg. The alloy was produced in the form of a ribbon thickness of 30 mu m using the melt spinning method, and its internal amorphous structure was examined by the X-ray diffraction method. The crystallization behavior of the alloy was studied using series of isothermal annealing of the samples of the alloy at temperatures in the range of 723-1023 K for different
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据