Amorphous materials; Oxides; Electron microscopy (TEM); Infrared spectroscopy (IR)
The effect of Ti addition in alumina carriers on the catalytic properties of corresponding supported-PdPt materials, as tested in liquid-phase dibenzothiophene (DBT) hydrodesulfurization (HDS) was studied. To that end, Al2O3-TiO2 materials (at Al/Ti = 25, 10, and 2, mol ratio) were synthesized by low-temperature sol gel method. Point of zero charge decreased by augmenting titania concentration in binary oxides, as to that of Al2O3. On the other hand, textural properties and Lewis acidity (as determined by FTIR of adsorbed pyridine) increased with TiO2 content in mixed supports. Noble metals were impregnated (nominal 1 wt%, Pd:Pt 4:1 mol ratio) on mixed supports and on reference alumina single oxide. Textural and surface modifications of alumina substrate provoked by titania addition resulted in improved metallic particles dispersion, as observed by High Resolution-TEM. Enhanced catalytic performance of noble metals-based materials with carriers of higher Ti-content was registered when tested in HDS reaction. In those cases, higher selectivity to products from hydrogenation reaction pathway was observed as well. Augmented medium and strong surface acidity and improved textural properties of carriers of enhanced TiO2 concentration seemed to play a major role in obtaining noble metals catalysts of improved hydrogenating properties. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据