MATERIALS CHARACTERIZATION
卷 113, 期 -, 页码 117-124出版社
ELSEVIER SCIENCE INC
DOI: 10.1016/j.matchar.2015.11.014
关键词
Martensite; Electron back scatter diffraction; Misorientation; X-ray diffraction; Dislocation density
类别
资金
- Hungarian Scientific Research Fund, OTKA [K-109021, PD-101028]
The microstructure and the dislocation density in as-quenched ferrous lath martensite were studied by different methods. The blocks, packets and variants formed due to martensitic transformation were identified and their sizes were determined by electron backscatter diffraction (EBSD). Concomitant transmission electron microscopy (TEM) investigation revealed that the laths contain subgrains with the size between 50 and 100 nm. A novel evaluation procedure of EBSD images was elaborated for the determination of the density and the space distribution of geometrically necessary dislocations from the misorientation distribution. The total dislocation density obtained by X-ray diffraction line profile analysis was in good agreement with the value determined by EBSD, indicating that the majority of dislocations formed due to martensitic transformation during quenching are geometrically necessary dislocations. (C) 2016 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据