Comparative Thermoelectric Properties of Polypropylene Composites Melt-Processed Using Pyrograf® III Carbon Nanofibers

The electrical conductivity (sigma) and Seebeck coefficient (S) at temperatures from 40 ffiC to 100 ffiC of melt-processed polypropylene (PP) composites filled with 5 wt.% of industrial-grade carbon nanofibers (CNFs) is investigated. Transmission Electron Microscopy (TEM) of the two Pyrograf (R) III CNFs (PR 19 LHT XT and PR 24 LHT XT), used in the fabrication of the PP/CNF composites (PP/CNF 19 and PP/CNF 24), reveals that CNFs PR 24 LHT XT show smaller diameters than CNFs PR 19 LHT XT. In addition, this grade (PR 24 LHT XT) presents higher levels of graphitization as deduced by Raman spectroscopy. Despite these structural differences, both Pyrograf (R) III grades present similar sigma (T) and S (T) dependencies, whereby the S shows negative values (n-type character). However, the sigma (T) and S (T) of their derivative PP/CNF19 and PP/CNF24 composites are not analogous. In particular, the PP/CNF24 composite shows higher sigma at the same content of CNFs. Thus, with an additionally slightly more negative S value, the PP/CNF24 composites present a higher power factor (PF) and figure of merit (zT) than PP/CNF19 composites at 40 degrees C. Moreover, while the sigma (T) and S (T) of CNFs PR 19 LHT XT clearly drive the sigma (T) and S (T) of its corresponding PP/CNF19 composite, the S (T) of CNFs PR 24 LHT XT does not drive the S (T) observed in their corresponding PP/CNF24 composite. Thus, it is inferred in PP/CNF24 composites an unexpected electron donation (n-type doping) from the PP to the CNFs PR 24 LHT XT, which could be activated when PP/CNF24 composites are subjected to that increase in temperature from 40 ffi C to 100 ffi C. All these findings are supported by theoretical modeling of sigma (T) and S (T) with the ultimate aim of understanding the role of this particular type of commercial CNFs on the thermoelectrical properties of their PP/CNF composites.

Automated summary

The electrical conductivity and Seebeck coefficient of melt-processed polypropylene composites filled with 5 wt.% of industrial-grade carbon nanofibers (CNFs) were investigated at temperatures from 40 ffiC to 100 ffiC. The structural differences of two types of Pyrograf (R) III CNFs resulted in different effects on the composite materials. The PP/CNF24 composite exhibited higher electrical conductivity and a more negative Seebeck coefficient compared to the PP/CNF19 composite, indicating better thermoelectric properties.