期刊
METALLOGRAPHY MICROSTRUCTURE AND ANALYSIS
卷 12, 期 3, 页码 427-432出版社
SPRINGERNATURE
DOI: 10.1007/s13632-023-00945-3
关键词
Pure zinc; KOBO extrusion; Point defect clusters; Modulated structure
In the study of zinc subjected to severe plastic deformation at low temperature using the KOBO extrusion method, three techniques of micro and nanostructure identification (TEM, STEM, HAADF) were employed. It was found that the long trails pattern observed in the microstructure after KOBO deformation resulted from strain fields of densely spaced nano-sized point defect clusters (SIA clusters). The presence of satellite spots on the diffraction pattern was explained by a periodic arrangement of clusters forming a modulated lattice with a nano-sized wavelength.
In the study of plastic flow and mechanical features of zinc subjected to severe plastic deformation at low temperature through the KOBO extrusion method, three techniques of micro and nanostructure identification have been used (TEM, STEM, HAADF). It was shown that the pattern of long trails-a typical element of microstructure after the KOBO deformation, results from strain fields of densely spaced nano-dimensional clusters of point defects-SIA clusters. The presence of satellite spots on the diffraction pattern was explained by a periodic arrangement of clusters which takes the form of a modulated lattice with a nano-sized wavelength.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据