Arabic Gum-Grafted-Hydrolyzed Polyacrylonitrile@ZnFe2O4 as a Magnetic Adsorbent for Remediation of Levofloxacin Antibiotic from Aqueous Solutions

期刊

ACS OMEGA
卷 -, 期 -, 页码 -

出版社

AMER CHEMICAL SOC
DOI: 10.1021/acsomega.2c06555

关键词

-

向作者/读者索取更多资源

The organic/inorganic adsorbent AG-g-HPAN@ZnFe2O4 was synthesized by grafting PAN onto Arabic gum in the presence of ZnFe2O4 magnetic nanoparticles and then hydrolyzing it with alkaline solution. The resulting adsorbent showed good thermal stability and superparamagnetic property. It exhibited uniform dispersion of zinc ferrite nanospheres throughout its smooth surface. The adsorption effectiveness of AG-g-HPAN@ZnFe2O4 for levofloxacin was investigated and it showed high adsorption capacity and good adsorption kinetics.
The Arabic gum-grafted-hydrolyzed polyacrylonitrile/ZnFe2O4 (AG-g-HPAN@ZnFe2O4) as organic/inorganic adsorbent was obtained in three steps using grafted PAN onto Arabic gum in the presence of ZnFe2O4 magnetic nanoparticles and then hydrolysis by alkaline solution. Fourier transform infrared (FT-IR), energy-dispersive X-ray analysis (EDX), field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), thermogravimetric analysis (TGA), vibrating sample magnetometer (VSM), and the Brunauer-Emmett-Teller (BET) analysis analyses were used to characterize the chemical, morphological, thermal, magnetic, and textural properties of the hydrogel nanocomposite. The obtained result demonstrated that the AG-g-HPAN@ZnFe2O4 adsorbent showed acceptable thermal stability with 58% char yields and superparamagnetic property with magnetic saturation (Ms) of 24 emu g-1. The XRD pattern showed that the semicrystalline structure with the presence of ZnFe2O4 has distinct peaks which displayed that the addition of zinc ferrite nanospheres to amorphous AG-g-HPAN increased its crystallinity. The AG-g-HPAN@ZnFe2O4 surface morphology exhibits uniform dispersion of zinc ferrite nanospheres throughout the smooth surface of the hydrogel matrix, and its BET surface area was measured at 6.86 m2/g, which was higher than that of AG-g-HPAN as a result of zinc ferrite nanosphere incorporation. The adsorption effectiveness of AG-g-HPAN@ZnFe2O4 for eliminating a quinolone antibiotic (levofloxacin) from aqueous solutions was investigated. The effectiveness of adsorption was assessed under several experimental conditions, including solution pH (2-10), adsorbent dose (0.0015-0.02 g) contact duration (10-60 min), and initial concentration (50-500 mg/L). The maximum adsorption capacity (Qmax) of the produced adsorbent for levofloxacin was found to be 1428.57 mg/g (at 298 k), and the experimental adsorption data were well explained by the Freundlich isotherm model. The pseudo-second-order model satisfactorily described the adsorption kinetic data. The levofloxacin was mostly adsorbed onto the AG-g-HPAN@ZnFe2O4 adsorbent via electrostatic contact and hydrogen bonding. Adsorption-desorption studies demonstrated that the adsorbent could be efficiently recovered and reused after four consecutive runs with no significant loss in adsorption performance.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据