期刊
LASERS IN MEDICAL SCIENCE
卷 31, 期 9, 页码 1837-1843出版社
SPRINGER LONDON LTD
DOI: 10.1007/s10103-016-2059-8
关键词
Alumina; Yttrium stabilized tetragonal zirconia poly crystal nano-composite; Femtosecond laser; Endosseous dental implant
Ceramic dental materials, especially alumina (20 %vol)-yttrium stabilized tetragonal zirconia poly crystal (A-Y-TZP20), have been considered as alternatives to metals for endosseous dental implant application. For increasing the bone-to-implant contact as well as the speed of bone formation, a new surface modification can be effective. The aim of this study was to design microgroove patterns by femtosecond laser on A-Y-TZP20 nano-composite disks for endosseous dental implant application. The phase composition and the morphology of the A-Y-TZP20 nano-composite samples were characterized using X-ray diffraction and Scanning electron microscopy equipped with energy dispersive X-ray spectroscopy techniques. Statistical analysis was submitted to Kolmogorov-Smirnov test and Student's t test for independent variables, with a 5 % significance level. EDAX analysis revealed a significant decrease in the relative content of contaminants like carbon (p < 0.05) in laser surface-treated group as compared to non surface-treated group. X-ray diffraction did not show any change in the crystalline structure induced by laser processing. It was concluded that the femtosecond laser is a clean and safe method for surface modification of A-Y-TZP20.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据