Effect of Heat Treatment on the Cavitation Erosion Behavior of Nanocrystalline Surface Layer of 304 Stainless Steel

期刊

APPLIED SCIENCES-BASEL
卷 13, 期 9, 页码 -

出版社

MDPI
DOI: 10.3390/app13095817

关键词

304 stainless steels; nanocrystalline layer; martensitic transformation; heat treatment; cavitation erosion

向作者/读者索取更多资源

In this study, a nanocrystalline layer composed primarily of martensite phase was prepared on the surface of 304 stainless steel. The cavitation erosion resistance of the nanocrystalline layer before and after heat treatment was investigated. The results showed that the nanocrystalline layer exhibited excellent erosion resistance, but the cavitation erosion performance decreased after heat treatment due to the decrease in hardness.
In this study, a nanocrystalline layer composed primarily of martensite phase was prepared on the surface of 304 stainless steel. Furthermore, the martensite phase content in the nanocrystalline layer was adjusted by heat treatment at 500 degrees C and 550 degrees C, respectively, and the cavitation erosion resistance of the nanocrystalline layer before and after heat treatment was investigated. The results showed that the nanocrystalline layer before and after heat treatment exhibited excellent erosion resistance, with cumulative mass loss of approximately 1/7, 1/5, and 1/3 that of the traditional 304 stainless steel, respectively. The nanocrystalline layer could significantly inhibit the growth of cavitation pits due to the high density of grain boundaries. However, due to the decrease in hardness of the nanocrystalline layer after heat treatment, the propagation speed of cavitation cracks was accelerated, and the cavitation erosion performance of the nanocrystalline layer showed a downward trend.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据