Research on the Cause and Control Method of Edge Warping Defect during Hot Finishing Rolling

期刊

METALS
卷 13, 期 3, 页码 -

出版社

MDPI
DOI: 10.3390/met13030565

关键词

edge warping; cause; control method; roll shape optimization; hot rolling

向作者/读者索取更多资源

Different from other profile defects, the edge warping defect is unique and its cause and control method are still unknown. By calculating the roll shape, it is found that the high-order comprehensive roll gap contour is the main cause of strip edge warping. Optimizing the original roll shape can effectively prevent the occurrence of edge warping defects.
Different from the cross-section profile defects caused by uneven roll wear or external forces during hot finishing rolling, the edge warping defect often occurs and has special local characteristics. However, the cause and control method of edge warping are still unclear. By superposition calculating the roll shape, it is found that the high-order comprehensive roll gap contour formed by the superposition of the bathtub-shaped roll thermal contour and parabolic original roll shape is the main cause of strip edge warping. To ensure that the comprehensive roll gap contour is parabolic rather than the original roll shape, the target curve of the comprehensive roll contour in the form of a parabola is determined according to the amplitude of the middle position of the comprehensive roll contour of the last strip in a standard rolling unit, and then subtract the thermal contour curve of the last strip to obtain the desired curve of the antithermal original roll shape. In theory and application, the optimization of the original roll shape can effectively avoid the occurrence of edge warping defect.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.5
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据