The Effect of a Nitrogen-Based Ionic Liquid as a Coating over 1Pd9Ag/Al2O3 for the Selective Hydrogenation of 1,7-Octadiene vs 1-Octene

期刊

CATALYSTS
卷 13, 期 4, 页码 -

出版社

MDPI
DOI: 10.3390/catal13040746

关键词

silver; palladium; selective hydrogenation; 1; 7-octadiene; [N-4444][NO3]; [EIM]; monolayer

向作者/读者索取更多资源

The effect of tetrabutylammonium nitrate as a surface coating over 1Pd9Ag/Al2O3 in the selective hydrogenation of 1,7-octadiene was studied. The results showed that the coating significantly decreased the conversion and selectivity of 1-octene. However, no net gain in 1-octene was observed. The thickness of the coating also affected the conversion and selectivity, with a thicker coating leading to further decline. Characterization of the catalysts confirmed leaching of the ionic liquid and re-establishment of the metal-support interaction.
The effect of tetrabutylammonium nitrate ([N-4444][NO3]) was studied as a surface coating over 1Pd9Ag/Al2O3 and applied in the selective hydrogenation of 1,7-octadiene in a mixture with 1-octene. Weight loadings up to a surface of three monolayers (MLs) were investigated and a further comparison coating with 1-ethylimidazole ([EIM]) was carried out to assess anionic effects in the Solid Catalysts with an Ionic Liquid Layer (SCILLs). Catalysts were characterised by H-2-chemisorption, TGA-DSC, BET measurements, XPS, and HR-TEM. Catalytic studies showed that the uncoated and EIM-coated (10 wt%) catalysts gave nearly a 100% conversion of 1,7-octadiene and 1-octene with a selectivity mainly towards octane. Coating with [N-4444][NO3] at 1 ML significantly decreased the 1-octene conversion by almost 50%, as well as the selectivity to octane (38%) at close to a 100% diene conversion. However, no net gain in 1-octene in the output stream was noted. At 2 ML IL/EIM coverage, a further decline in 1-octene conversion and octane selectivity was found at a diene conversion of 75%. The selectivity to 1-octene steadily increased from over the bare catalyst (52%) to the EIM-coated (62%) catalyst and SCILL (75%). At 3 ML IL coverage, the diene conversion (35%) was significantly reduced due to mass transfer limitations of hydrogen through the thick IL layer. Characterisation of the used catalysts by TG and BET analyses confirmed a leaching of up to 14% of the ionic liquid in the SCILLs coated at 1 ML and 2 ML, with an increase in surface area noted. Furthermore, smaller particle sizes of the used catalysts showed that the metal-support interaction was re-established. These results confirm a mild ligand coordination between the nitrogen in the IL anion and Pd and Ag where the ionic liquid remained physisorbed over the surface of the catalyst. In addition, component miscibility tests revealed partial solubility of the diene in the ionic liquid, indicating the presence of solvent effects also.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据