Trajectory Strategy Effects on the Material Characteristics in the WAAM Technique

The wire Arc Additive Manufacturing (WAAM) technique has evolved into a cutting-edge 3D printing technique. This study surveys the influences of trajectory on the characteristics of low-carbon steel samples generated by the WAAM technique. The results show that the grains in the WAAM samples are isotropic, with grain size numbers ranging from 7 to 12. Strategy 3, with a spiral trajectory, has the smallest grain size, while strategy 2, with a lean zigzag trajectory, has the largest. The variations in grain size are caused by differences in heat input and output during the printing process. The WAAM samples achieve a significantly higher UTS value than the original wire, demonstrating the WAAM technique's benefit. Strategy 3, with a spiral trajectory, achieves the highest UTS value, 616.5 MPa, 24% higher than the original wire. The UTS values of strategy 1 (horizontal zigzag trajectory) and strategy 4 (curve zigzag trajectory) are comparable. WAAM samples have significantly higher elongation values than the original wire, with only 22% elongation. The sample with the highest elongation value, 47.2%, was produced by strategy 3. Strategy 2 has an elongation value of 37.9%. The value of elongation is proportional to the value of UTS. WAAM samples have average elastic modulus values of 95.8 GPa, 173.3 GPa, 92.2 GPa, and 83.9 GPa, corresponding to strategies 1, 2, 3, and 4. Only a strategy 2 sample has a similar elastic modulus value to the original wire. All samples have dimples on the fracture surface, indicating that the WAAM samples are ductile. These fracture surfaces' equiaxial shape corresponds to the original microstructure's equiaxial shape. The results provide the optimal trajectory for the WAAM products is the spiral trajectory, while the lean zigzag trajectory gains only modest characteristics.

Automated summary

The study examines the effects of trajectory on low-carbon steel samples produced by the wire Arc Additive Manufacturing (WAAM) technique. The results show that the grain size of the WAAM samples ranges from 7 to 12, with strategy 3 (spiral trajectory) having the smallest grain size and strategy 2 (lean zigzag trajectory) having the largest. Differences in heat input and output during the printing process contribute to the variations in grain size. The WAAM samples demonstrate significantly higher ultimate tensile strength (UTS) values compared to the original wire, with strategy 3 achieving the highest UTS value of 616.5 MPa, 24% higher than the original wire. The WAAM samples also have higher elongation values and exhibit ductile fracture surfaces with dimples.