DOI: 10.3390/polym15102387
关键词
denture base polymers; cross-linking agent; flexural strength; impact strength; surface hardness
This study investigated the effects of different cross-linking agents with varying chain lengths and flexibilities on the mechanical properties of PMMA. The results showed that there was no significant increase in flexural strength, elastic modulus, or impact strength with the addition of cross-linking agents. However, the surface hardness of PMMA notably decreased with the addition of PEGDMA in concentrations ranging from 5% to 20%. The incorporation of cross-linking agents in concentrations ranging from 5% to 15% led to an improvement in the mechanical properties of PMMA.
Cross-linking agents are incorporated into denture base materials to improve their mechanical properties. This study investigated the effects of various cross-linking agents, with different cross-linking chain lengths and flexibilities, on the flexural strength, impact strength, and surface hardness of polymethyl methacrylate (PMMA). The cross-linking agents used were ethylene glycol dimethacrylate (EGDMA), tetraethylene glycol dimethacrylate (TEGDMA), tetraethylene glycol diacrylate (TEGDA), and polyethylene glycol dimethacrylate (PEGDMA). These agents were added to the methyl methacrylate (MMA) monomer component in concentrations of 5%, 10%, 15%, and 20% by volume and 10% by molecular weight. A total of 630 specimens, comprising 21 groups, were fabricated. Flexural strength and elastic modulus were assessed using a 3-point bending test, impact strength was measured via the Charpy type test, and surface Vickers hardness was determined. Statistical analyses were performed using the Kolmogorov-Smirnov Test, Kruskal-Wallis Test, Mann-Whitney U Test, and ANOVA with post hoc Tamhane test (p <= 0.05). No significant increase in flexural strength, elastic modulus, or impact strength was observed in the cross-linking groups compared to conventional PMMA. However, surface hardness values notably decreased with the addition of 5% to 20% PEGDMA. The incorporation of cross-linking agents in concentrations ranging from 5% to 15% led to an improvement in the mechanical properties of PMMA.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据