Effect of Bioactive Filler Addition on the Mechanical and Biological Properties of Resin-Modified Glass Ionomer

The maintenance of affected dentin can promote the greater conservation of tooth structure. The development of materials that have properties capable of reducing the demineralizing potential and/or even helping in dental remineralization is important for conservative dentistry. This study aimed to evaluate, in vitro, the alkalizing potential, fluoride as well as calcium ion release ability, antimicrobial activity, and dentin remineralization properties of resin-modified glass ionomer cement (RMGIC) incorporated with a bioactive filler (niobium phosphate (NbG) and bioglass (45S5)). The study samples were grouped into RMGIC, NbG, and 45S5. The materials' alkalizing potential, ability to release calcium as well as fluoride ions, and antimicrobial properties concerning Streptococcus mutans UA159 biofilms were analyzed. The remineralization potential was evaluated using the Knoop microhardness test, which was performed at different depths. The alkalizing and fluoride release potential was higher for the 45S5 group (p < 0.001) over time. An increase in the microhardness of demineralized dentin was observed in the 45S5 and NbG groups (p < 0.001). No differences in biofilm formation were observed between the bioactive materials, although 45S5 exhibited lower biofilm acidogenicity at different time points (p < 0.001) and greater calcium ion release in the microbial environment. A resin-modified glass ionomer cement enriched with bioactive glasses, particularly 45S5, is a promising alternative for the treatment of demineralized dentin.

Automated summary

The study aimed to evaluate the properties of resin-modified glass ionomer cement (RMGIC) incorporated with a bioactive filler (niobium phosphate (NbG) and bioglass (45S5)) for dental remineralization. The alkalizing potential, fluoride and calcium ion release ability, antimicrobial activity, and dentin remineralization properties were analyzed in vitro. The results showed that 45S5 exhibited higher alkalizing and fluoride release potential, and both 45S5 and NbG groups promoted the microhardness of demineralized dentin.