Effects of Cr Content on Microstructure and Mechanical Properties of Co-Free FeCryNiAl0.8 High-Entropy Alloys

High-entropy alloys have gained widespread concern in response to the increased requirements for future high-temperature structural superalloys. By combining phase-diagram calculations with microhardness, compression behavior measurements at room temperature, and elevated temperature conditions, the very important role of the Cr element on the microstructure and properties is deeply revealed, which provides candidates materials for future high-temperature alloy applications. The increment of Cr favors the regulation of the two-phase fraction and distribution. The thermodynamic calculations illustrate that the density and melting point of the HEAs showed an increasing trend with the increase of the Cr content. The typical worm-like microstructure of the Cr-0.6 alloy with a dual BCC structure was detected. Meanwhile, on the one hand, the increment of the Cr elements results in a considerable optimization of the mechanical properties of the alloy in terms of strength and ductility at room temperature. The corresponding compressive strength and plasticity of Cr-0.6 alloy at room temperature are 3524 MPa and 43.3%. On the other hand, the high-temperature mechanical properties of the alloy are greatly enhanced. At 1000 degrees C, the yield strength of the Cr-0.6 alloy is about 25 MPa higher than that of the Cr-0.4 alloy. The superior mechanical properties are attributed to the pronounced work-hardening response, and the work-hardening behavior of Cr-containing HEAs was systematically analyzed by employing the modified Ludwik model. The higher content of Cr helps the resistance of the local deformation response, improving the nonuniform strain and promoting the balance of strength and ductility of the alloys.

Automated summary

High-entropy alloys have gained attention as potential materials for future high-temperature structural superalloys. The role of the Cr element in microstructure and properties has been revealed, showing significant improvement in strength and ductility. The density and melting point of the alloys increase with higher Cr content. The mechanical properties, including compressive strength and plasticity, are optimized, and the high-temperature mechanical properties are greatly enhanced.