Comparison of (K0.5Na0.5)NbO3 Single Crystals Grown by Seed-Free and Seeded Solid-State Single Crystal Growth

(K0.5Na0.5)NbO3-based piezoelectric ceramics are of interest as a lead-free replacement for Pb(Zr,Ti)O-3. In recent years, single crystals of (K0.5Na0.5)NbO3 with improved properties have been grown by the seed-free solid-state crystal growth method, in which the base composition is doped with a specific amount of donor dopant, inducing a few grains to grow abnormally large and form single crystals. Our laboratory experienced difficulty obtaining repeatable single crystal growth using this method. To try and overcome this problem, single crystals of 0.985(K0.5Na0.5)NbO3-0.015Ba(1.05)Nb(0.77)O(3) and 0.985(K0.5Na0.5)NbO3-0.015Ba(Cu0.13Nb0.66)O-3 were grown both by seed-free solid-state crystal growth and by seeded solid-state crystal growth using [001] and [110]-oriented KTaO3 seed crystals. X-ray diffraction was carried out on the bulk samples to confirm that single-crystal growth had taken place. Scanning electron microscopy was used to study sample microstructure. Chemical analysis was carried out using electron-probe microanalysis. The single crystal growth behaviour is explained using the mixed control mechanism of grain growth. Single crystals of (K0.5Na0.5)NbO3 could be grown by both seed-free and seeded solid-state crystal growth. Use of Ba(Cu0.13Nb0.66)O-3 allowed a significant reduction in porosity in the single crystals. For both compositions, single crystal growth on [001]-oriented KTaO3 seed crystals was more extensive than previously reported in the literature. Large (similar to 8 mm) and relatively dense (<8% porosity) single crystals of 0.985(K0.5Na0.5)NbO3-0.015Ba(Cu0.13Nb0.66)O-3 can be grown using a [001]-oriented KTaO3 seed crystal. However, the problem of repeatable single crystal growth remains.

Automated summary

In this study, (K0.5Na0.5)NbO3-based single crystals were successfully grown using both seed-free solid-state crystal growth and seeded solid-state crystal growth methods. It was found that using Ba(Cu0.13Nb0.66)O-3 could significantly reduce the porosity in the single crystals. However, the problem of repeatable single crystal growth remains.