A facile green approach to the synthesis of Bi2WO6@V2O5 heterostructure and their photocatalytic activity evaluation under visible light irradiation for RhB dye removal

Bismuth tungsten oxide and vanadium pentoxide (Bi2WO6/V2O5) heterostructures are produced by a green synthesis approach using Azadirachta indica extract for photocatalytic perfor-mance. The hydrothermal method at temperatures between 120 degrees C and 140 degrees C is used to synthesize Bi2WO6. Bi2WO6 and V2O5 phases are formed in pure orthorhombic wells according to the XRD pattern. The SEM displays V2O5 nanorods, Bi2WO6 hierarchical microspheres that resemble flow-ers at 120 degrees C, and particles with a particle-like character at 140 degrees C. In V2O5, the asymmetric stretch-ing vibrations of the triplely coordinated oxygen (chain oxygen) bonds and the vibration of the doubly coordinated oxygen (bridge oxygen) bonds are responsible for a peak at 611 cm -1. In FTIR spectra between 600 and 1600 cm -1, the major absorption bands in Bi2WO6 are attributed to the W-O stretching, Bi-O stretching, and W-O-W bridging stretching modes. Bi2WO6@V2O5 at 120 degrees C has the lowest bandgap energy (2.32 eV) and optical electronegativity (0.62), as well as the highest refractive index (2.57), extinction coefficient (2.21), and dielectric constant (er = 0.72 and ei = 11.4) among all samples, making it a suitable material for photocatalysis. Rhodamine blue (RhB) dye degradation is used to measure the photocatalytic activity (PCA) of certain materials. The results showed that heterostructure V2O5@Bi2WO6 synthesized at 120 degrees C is more attractive among all samples due to high degradation of RhB dye under sunlight irradiation in 90 min. (c) 2023 The Author(s). Published by Elsevier B.V. on behalf of King Saud University. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).

Automated summary

Bismuth tungsten oxide and vanadium pentoxide (Bi2WO6/V2O5) heterostructures were synthesized using Azadirachta indica extract for photocatalytic performance. Bi2WO6 was synthesized using the hydrothermal method at temperatures between 120 degrees C and 140 degrees C. The synthesized materials exhibited different morphologies at different temperatures. Bi2WO6@V2O5 at 120 degrees C showed the highest photocatalytic activity, making it a suitable material for photocatalysis.