Effect of Ni substitution on the antiferromagnetic domains of cobalt oxide

We present a spatially resolved X-ray magnetic linear dichroism study of high quality micron-sized mixed nickel-cobalt oxide (NCO) crystals. NixCo1-xO was prepared in-situ by high-temperature oxygen-assisted molecular beam epitaxy on a Ru(0001) single crystal substrate. To check the effect of incorporating Ni into the cobalt oxide films, three different compositions were prepared. The element-specific XMLD measurements reveal strong antiferromagnetic contrast at room temperature and magnetic domains up to one micron size, reflecting the high structural quality of the NCO islands. By means of vectorial magnetometry, the antiferromagnetic spin axis orientation of the domains was determined with nanometer spatial resolution, and found to depend on the stoichiometry of the prepared crystals.

Automated summary

We conducted a spatially resolved X-ray magnetic linear dichroism study on high quality micron-sized mixed nickel-cobalt oxide (NCO) crystals. NixCo1-xO was prepared in-situ by high-temperature oxygen-assisted molecular beam epitaxy on a Ru(0001) single crystal substrate. Three different compositions were prepared to examine the effect of incorporating Ni into the cobalt oxide films. The element-specific XMLD measurements showed strong antiferromagnetic contrast at room temperature, with magnetic domains up to one micron size, indicating the high structural quality of the NCO islands.