4.5 Article

Solution processed low operating voltage SnO2 thin film transistor by using Li2SnO3/TiO2 stacked gate dielectric

出版社

ELSEVIER
DOI: 10.1016/j.mseb.2023.116270

关键词

Thin film transistor; Metal oxide; Sol-gel; Ionic dielectric; Low operating voltage

向作者/读者索取更多资源

A thin layer of sol-gel derived lithium stannate (Li2SnO3) with low DC conductivity and high areal capacitance was deposited using a spin coating method. Adding a sol-gel derived titanium-oxide (TiO2) layer further reduced the DC conductivity of the Li2SnO3 thin film. The bilayer thin film of Li2SnO3/TiO2 exhibited increased effective areal capacitance and met the requirement for a low operating voltage thin film transistor (TFT) gate dielectric.
A thin layer of sol-gel derived lithium stannate (Li2SnO3) was deposited by a spin coating method that shows high areal capacitance with low DC conductivity which originated due to the mobile lithium ion (Li+) and low carrier concentration. The DC conductivity of this Li2SnO3 thin film has been reduced further by adding a sol-gel derived titanium-oxide (TiO2) layer. Moreover, bilayer thin film effective areal capacitance also increases due to the higher relative permittivity of TiO2 layer. The measured areal capacitance of such Li2SnO3 /TiO2 bilayer thin films is 518 nF/cm(2) with a low current density of 3.8 X 10(-5) A/cm(2) under 5 V external bias, can fulfil the requirement as gate dielectric of a low operating voltage (<= 3V) thin film transistor (TFT). For identifying its applicability as gate insulator, a solution-processed tin oxide (SnO2) thin film transistor (TFT) was fabricated with Li2SnO3/TiO2 stacked gate dielectric. In this TFT structure, thin film of TiO2, SnO2 and Li2SnO3 are all polycrystalline in nature. The electrical characterization of TFT has been done under DC mode operation in ambient atmosphere measurement which remain almost unaltered under 11 cyclic measurements. The optimized TFT required only 3.0 V external bias that shows an electron mobility of 3.47 cm(2) V-1 s(-1) with on/off ratio of 50.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.5
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据