Aluminium alloys; Heat -resistance; Ternary eutectic; Mechanical properties; High pressure die casting
Microstructures and mechanical properties of near-eutectic and hypoeutectic Al-Si-Ni-Fe-Mn alloys were studied under as-cast condition. The alloys exhibited primary intermetallic phases, with different precipitates and lattice parameters. These alloys showed excellent mechanical properties at high temperatures, making them suitable for industrial applications.
Microstructures and mechanical properties of near-eutectic and hypoeutectic Al-Si-Ni-Fe-Mn alloys were studied under as-cast condition. Near-eutectic 78Al15Si4Ni2.5Fe0.5Mn (wt.%) and hypoeutectic 83.6Al11Si3Ni1.9Fe0.5Mn (wt.%) alloys were processed by high pressure die casting. These two alloys have the same ternary eutectic mixture of & alpha;-Al, Si and Al6(FeNiMn) with a melting point of 567 degrees C. Primary intermetallic phases of block-like Al17(FeNiMn)4Si and plate-like Al4(FeNiMn)Si2 in these two alloys were observed. Precipitates of Si and Ni-contained phase coexist in primary & alpha;-Al grains of hypoeutectic alloy. The lattice parameters of Al6(FeNiMn), Al17(FeNiMn)4Si, and Al4(FeNiMn)Si2 phases are slightly changed compared with orthorhombic Al3Ni, orthorhombic Al5.6Fe2 and tetragonal FeAl3Si2 phases from the database, respectively. These two alloys have excellent mechanical properties at high temperatures. The ultimate tensile strength (UTS) at 300 degrees C ranges from 135 & PLUSMN; 6 MPa (hypoeutectic alloy) to 157 & PLUSMN; 6 MPa (near-eutectic alloy), which is superior to commercial A383 alloy and some other heat-resistant alloys. Therefore, these near-eutectic and hypoeutectic Al-Si-Ni-Fe-Mn alloys have huge potential for industrial application at elevated temperatures.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据