Amorphous materials; Nanocrystalline materials; Microalloying; Magnetic materials
Novel Fe86-xP11C2B1Inx (x = 0, 0.2, 0.4, 0.6, 0.8 and 1) amorphous alloys were developed in this study. After appropriate annealing, Fe85.8P11C2B1In0.2 nanocrystalline alloy with low coercivity (2.9-21.0 A/m) and high saturation magnetization (1.63-1.73 T) was obtained. The nanocrystalline structure was confirmed by XRD and TEM, and In microalloying was found to induce nanocrystallization in FePCB amorphous alloy according to Kissinger's plot. This provides a new approach for developing Fe-based nanocrystalline soft magnetic alloys.
In this work, novel Fe86-xP11C2B1Inx (x = 0, 0.2, 0.4, 0.6, 0.8 and 1) amorphous alloys were developed. After proper annealing of the amorphous precursor, Fe85.8P11C2B1In0.2 nanocrystalline alloy, with relatively low coercivity (Hc) and high saturation magnetization (Bs) in the range of 2.9-21.0 A/m and 1.63-1.73 T, was ob-tained. The structure of the nanocrystalline structure was investigated and confirmed by XRD and TEM. The results indicate that In microalloying can induce the nanocrystallization in FePCB amorphous alloy, which was proved by Kissinger's plot. It provides a new way to develop new Fe-based nanocrystalline soft magnetic alloys.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据