Effects of stoichiometry and individual layer thickness ratio on the quality of epitaxial CrBx/TiBy superlattice thin films

Studies of single crystal artificial superlattices (SLs) of transition-metal (TM) diborides, which is instru- mental to understand hardening mechanisms at nanoscale, is lacking. Here, CrBx/TiBy (0001) diboride SLs [x,y E 1.7-3.3] are grown epitaxially on Al2O3(0001) substrates by direct-current magnetron sputter epitaxy. Growth conditions for obtaining well-defined SLs with good interface quality are found at 4 mTorr Ar pressure and 600 degrees C. 1 -mu m-thick SL films deposited with modulation periods A between 1 and 10 nm, and A=6 nm SLs with TiBy-to-A layer thickness ratios F ranging from 0.2 to 0.8 are studied. SLs with A=6 nm and F in the range of 0.2-0.4, with a near stoichiometric B/TM ratio, exhibit the high- est structural quality. The effects of F and stoichiometries (B/TM ratio) on the distribution of B in the SL structures are discussed. By increasing the relative thickness of TiBy, the crystalline quality of SLs starts to deteriorate due to B segregation in over-stoichiometric TiBy, resulting in narrow epitaxial SL columnar growth with structurally-distorted B-rich boundaries. Moreover, increasing the relative thickness of under-stoichiometric CrBx enhances the SL quality and hinders formation of B-rich boundaries. The SLs are found to exhibit hardness values in the range of 29-34 GPa.(c) 2023 The Author(s). Published by Elsevier Ltd. This is an open access article under the CC BY license (http://creativecommons.org/licenses/by/4.0/).

Automated summary

In this study, CrBx/TiBy (0001) diboride superlattices were grown epitaxially on Al2O3 substrates using direct-current magnetron sputter epitaxy. The effects of period and B/TM ratio on the structural quality were investigated. It was found that increasing the relative thickness of TiBy improved the superlattice quality but excessive TiBy led to structural distortion. On the other hand, increasing the relative thickness of CrBx enhanced the superlattice quality and hindered the formation of B-rich boundaries. The hardness values of the superlattices ranged from 29-34 GPa.